High transparency Cr,Nd:LuAG ceramics prepared with MgO additive
Zhang, Pande; Chai, Baoyan; Jiang, Benxue; Jiang, Yiguang; Chen, Shuilin; Gan, Qijun; Fan, Jintai; Mao, Xiaojian; Zhang, Long; jiangsic@foxmail.com; lzhang@siom.ac.cn
2017
Source PublicationJ. Eur. Ceram. Soc.
Volume37Issue:6Pages:2459
AbstractCr (0.2 at.%) and Nd (0.8 at.%) co-doped Lu3Al5O12 ceramics were fabricated with MgO as the sintering additive. The addition of a small amount of MgO can affect the grain boundary mobility and influence the number and location of micropores in ceramics during the sintering process. The results show that when the MgO content is 0.02 wt.%, high-transparency Cr,Nd:LuAG ceramics can be obtained by vacuum sintering at 1670 degrees C for 5 h followed by hot isostatic pressing (HIP) post-sintering at 1750 degrees C in an argon atmosphere (P = 200 MPa) for 5 h. The optimum in-line transmittance of the HIPed Cr,Nd:LuAG ceramics (3 mm thick) is 83.5% at a wavelength of 840 nm and 84.0% at 710 nm. (C) 2017 Published by Elsevier Ltd.
SubtypeArticle
Department材料
DOI10.1016/j.jeurceramsoc.2017.01.023
Funding OrganizationNational Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS ; National Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS ; National Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS ; National Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS
Indexed BySCI
Funding OrganizationNational Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS ; National Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS ; National Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS ; National Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS
WOS IDWOS:000397359300017
Citation statistics
Cited Times:5[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.siom.ac.cn/handle/181231/28095
Collection中科院强激光材料重点实验室
Corresponding Authorjiangsic@foxmail.com; lzhang@siom.ac.cn
Affiliation中国科学院上海光学精密机械研究所
Recommended Citation
GB/T 7714
Zhang, Pande,Chai, Baoyan,Jiang, Benxue,et al. High transparency Cr,Nd:LuAG ceramics prepared with MgO additive[J]. J. Eur. Ceram. Soc.,2017,37(6):2459.
APA Zhang, Pande.,Chai, Baoyan.,Jiang, Benxue.,Jiang, Yiguang.,Chen, Shuilin.,...&lzhang@siom.ac.cn.(2017).High transparency Cr,Nd:LuAG ceramics prepared with MgO additive.J. Eur. Ceram. Soc.,37(6),2459.
MLA Zhang, Pande,et al."High transparency Cr,Nd:LuAG ceramics prepared with MgO additive".J. Eur. Ceram. Soc. 37.6(2017):2459.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, Pande]'s Articles
[Chai, Baoyan]'s Articles
[Jiang, Benxue]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, Pande]'s Articles
[Chai, Baoyan]'s Articles
[Jiang, Benxue]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, Pande]'s Articles
[Chai, Baoyan]'s Articles
[Jiang, Benxue]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.