Fabrication of transparent La-doped Y2O3 ceramics using different La2O3 precursors
Li, Xiaokai; Mao, Xiaojian; Feng, Minghui; Qi, Shen; Jiang, Benxue; Zhang, Long; xmao@siom.ac.cn; lzhang@siom.ac.cn
2016
发表期刊J. Eur. Ceram. Soc.
卷号36期号:10页码:2549
摘要Despite being the most common sintering additive of transparent Y2O3 ceramics, La2O3 still suffers from weight changes when used in manufacturing processes due to its absorption of moisture and carbon dioxide. In the present work, two stable precursors, La(OH)(3) and La2O2CO3, were proposed for use as sintering additives for transparent Y2O3 ceramics; La2O3 powder was used for comparison. A series of experiments were conducted to investigate the influences of La2O3, La(OH)(3) and La2O2CO3 on the optical properties of Y2O3 ceramics by comparing the properties of mixed powders, green bodies and their sintering behaviors. Samples using La(OH)(3) or La2O2CO3 as sintering additives exhibited more favorable optical properties at similar sintering temperatures compared to those using La2O3. Transmittances close to the theoretical value at 4 mu m were achieved for samples doped with La(OH)(3) or La2O2CO3 sintered at 1800 degrees C. (C) 2016 Elsevier Ltd. All rights reserved.
文章类型Article
部门归属材料
DOI10.1016/j.jeurceramsoc.2016.03.024
资助者National Youth Natural Science Foundation of China [51302284, 6140031038] ; National Youth Natural Science Foundation of China [51302284, 6140031038] ; National Youth Natural Science Foundation of China [51302284, 6140031038] ; National Youth Natural Science Foundation of China [51302284, 6140031038]
收录类别SCI
资助者National Youth Natural Science Foundation of China [51302284, 6140031038] ; National Youth Natural Science Foundation of China [51302284, 6140031038] ; National Youth Natural Science Foundation of China [51302284, 6140031038] ; National Youth Natural Science Foundation of China [51302284, 6140031038]
WOS记录号WOS:000375518700017
引用统计
被引频次:12[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.siom.ac.cn/handle/181231/28076
专题中科院强激光材料重点实验室
通讯作者xmao@siom.ac.cn; lzhang@siom.ac.cn
作者单位中国科学院上海光学精密机械研究所
推荐引用方式
GB/T 7714
Li, Xiaokai,Mao, Xiaojian,Feng, Minghui,et al. Fabrication of transparent La-doped Y2O3 ceramics using different La2O3 precursors[J]. J. Eur. Ceram. Soc.,2016,36(10):2549.
APA Li, Xiaokai.,Mao, Xiaojian.,Feng, Minghui.,Qi, Shen.,Jiang, Benxue.,...&lzhang@siom.ac.cn.(2016).Fabrication of transparent La-doped Y2O3 ceramics using different La2O3 precursors.J. Eur. Ceram. Soc.,36(10),2549.
MLA Li, Xiaokai,et al."Fabrication of transparent La-doped Y2O3 ceramics using different La2O3 precursors".J. Eur. Ceram. Soc. 36.10(2016):2549.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Li, Xiaokai]的文章
[Mao, Xiaojian]的文章
[Feng, Minghui]的文章
百度学术
百度学术中相似的文章
[Li, Xiaokai]的文章
[Mao, Xiaojian]的文章
[Feng, Minghui]的文章
必应学术
必应学术中相似的文章
[Li, Xiaokai]的文章
[Mao, Xiaojian]的文章
[Feng, Minghui]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。