Crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal
Di, J. Q.; Xu, X. D.; Xia, C. T.; Zheng, L. H.; Aka, G.; Yu, H. H.; Sai, Q. L.; Guo, X. Y.; Zhu, L.; jvqing.di@vitalchem.com; xdxu79@mail.sic.ac.cn; xia_ct@siom.ac.cn
2016
发表期刊Laser Phys.
卷号26期号:4
摘要In this paper, the crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal were reported. The segregation coefficient of Yb3+ ions was calculated to be 0.47. The cell parameters were determined to be a = b = 0.3658 nm, c = 1.1985 nm. The peak absorption cross-section was calculated to be 2.65 x 10(-20) cm(2) at 979 nm and the peak stimulated emission cross-section was 2.23 x 10(-20) cm(2) at 980 nm for the p polarization. The continuous-wave (CW) laser operations of uncoated Yb:CaGdAlO4 crystals with 5 x 5 x 3 mm(3) in size were demonstrated. A maximum output power of 1.6 W at 1048 nm was obtained with a slope efficiency of 28%. The results show that Yb: CaGdAlO4 crystal is a promising laser medium.
文章类型Article
部门归属材料
DOI10.1088/1054-660X/26/4/045803
资助者Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700] ; Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700] ; Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700] ; Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700]
收录类别SCI
资助者Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700] ; Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700] ; Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700] ; Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700]
WOS记录号WOS:000375157900018
引用统计
被引频次:7[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.siom.ac.cn/handle/181231/28043
专题中科院强激光材料重点实验室
通讯作者jvqing.di@vitalchem.com; xdxu79@mail.sic.ac.cn; xia_ct@siom.ac.cn
作者单位中国科学院上海光学精密机械研究所
推荐引用方式
GB/T 7714
Di, J. Q.,Xu, X. D.,Xia, C. T.,et al. Crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal[J]. Laser Phys.,2016,26(4).
APA Di, J. Q..,Xu, X. D..,Xia, C. T..,Zheng, L. H..,Aka, G..,...&xia_ct@siom.ac.cn.(2016).Crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal.Laser Phys.,26(4).
MLA Di, J. Q.,et al."Crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal".Laser Phys. 26.4(2016).
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Di, J. Q.]的文章
[Xu, X. D.]的文章
[Xia, C. T.]的文章
百度学术
百度学术中相似的文章
[Di, J. Q.]的文章
[Xu, X. D.]的文章
[Xia, C. T.]的文章
必应学术
必应学术中相似的文章
[Di, J. Q.]的文章
[Xu, X. D.]的文章
[Xia, C. T.]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。