| 高温无机闪烁晶体Ce：YAlO_3的缺陷研究 | |
| Alternative Title | Investigation on defects in the high temperature inorganic scintillation single crystals of Ce:YAlO_3 |
| 赵广军; 李涛; 何晓明; 徐军; 田玉莲; 黄万霞 | |
| 2002 | |
| Source Publication | 核技术
 |
| Volume | 25Issue:10Pages:869 |
| Abstract | 采用同步辐射白光透射形貌术研究了提拉法生长的高温无机闪烁晶体Ce:YAlO_3（简称Ce:YAP）中的缺陷。实验发现在Ce:YAP晶体中存在着生长条纹、包裹沉积物、核心、孪晶及位错簇等缺陷，同时对生长缺陷形成的原因进行了讨论。结果表明，离子掺杂浓度、原料的纯度以及生长工艺条件等是影响Ce:YAP晶体缺陷的主要原因。 |
| Subtype | Article |
| Other Abstract | The defects in Ce: YAlO_3 single crystals grown by Czochralski method were investigated by transmission white beam synchrotron radiation topography method. It was shown in experiments that the growth striations, inclusions precipitations, twins, core and dislocation group were the main growth defects in Ce: YAP single crystals. The mechanism of the defects formation was also discussed in the paper. The results showed that the doped concentration, purity of starting materials and growth conditions are the main causes for defects formation in Ce:YAP single crystals. |
| Indexed By | CSCD |
| Language | 中文 |
| CSCD ID | CSCD:1002818 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Version | 出版稿 |
| Identifier | http://ir.siom.ac.cn/handle/181231/17968 |
| Collection | 激光与光电子功能材料研发中心 |
| Affiliation | 1.赵广军, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 2.李涛, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 3.何晓明, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 4.徐军, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 5.田玉莲, 中国科学院高能物理研究所, 北京 100039, 中国. 6.黄万霞, 中国科学院高能物理研究所, 北京 100039, 中国. |
| Recommended Citation GB/T 7714 | 赵广军,李涛,何晓明,等. 高温无机闪烁晶体Ce：YAlO_3的缺陷研究[J]. 核技术,2002,25(10):869. |
| APA | 赵广军,李涛,何晓明,徐军,田玉莲,&黄万霞.(2002).高温无机闪烁晶体Ce：YAlO_3的缺陷研究.核技术,25(10),869. |
| MLA | 赵广军,et al."高温无机闪烁晶体Ce：YAlO_3的缺陷研究".核技术 25.10(2002):869. |
| Files in This Item: | ||||||
| File Name/Size | DocType | Version | Access | License | ||
| 高温无机闪烁晶体Ce：YAlO_3的缺陷（174KB） | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | Application Full Text | |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment